LLDPE


LLDPE: LL0209AA


PRODUCT DESCRIPTION

  •  “LL 0209AA” is a LLDPE copolymer with butene as
 comonomer which contains antioxidant.
  • Recommended for general purpose applications.
  • Suitable for blending with conventional LDPE.

Film made from pure LL 02090 AA has the following 
advantages over conventional LDPE:

  • Better sealing,higher puncture resistance.
  • Greater drawdown capability.
  • Higher tensile strength.

Neutralizer: Calcium Stearate
Antioxidant: Irganox1010, Irganox168

APPLICATIONS
  • Food Grade
  • Heavy Duty Sacks
  •  Agricultural Films
  • Liners
  • Produce Bags
  • Stretch Films


Property
Value
Units
Test Method
  Density                                   920                   Kg/m3            ISO 1181
  Melt Index (190°C/2.16Kg)       0.9                    g/10min         ISO 1133
  Tensile Strength at Yield          10/11                 MPa              ISO 527
  MD/TD
 Tensile Strength at Break          620/840             %                 ISO 527
 MD/TD
 Tear Strength MD/TD               145/370            g/25µ            ASTM D1922
 Dart Drop Impact                     130                   g                  ASTM        D1709

Note: typical properties, not to be construed as specifications.



LLDPE: 22501AA/22501KJ



PRODUCT DESCRIPTION
  • 22501 is a LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion temperature. This resin combines ease of processing with low gels and it is well suited for blending with LDPE and for general purpose applications. 

FEATURES
  • High Stiffness
  • Good Optical Properties
  • Low Extrusion Temperature 
  • Ease of Processing
  • Low Gels 
  • Suited for Blending with LDPE
  • General Purpose Applications

APPLICATIONS
  • Blown Film Grade

ADDITIVES
  • 22501AA: Thermal Antioxidant
  • 22501KJ: Thermal Antioxidant, Antiblocking Agent, Slip Agent 

RECOMMENDED PROCESSING CONDITIONS
  • Melt Temperature (°C): 190-230
  • low up Ration: 2.0-3.0
  • Die Gap (mm): 2.0-2.5
  • Thickness (micron): 15-150


Resin Property
Value
Units
Test Method
   Density                                0.9220             g/cm3                   D 1505
   Melt Index                            0.95                 g/10 min              D 1238
Film Properties
  Dart Impact                           80                   g                         D 1709
  Elmendorf Tear MD/TD          105/460           g                          D 1922
  Tensile Strength at Break       45/30              MPa                      D 882
   MD/TD  
  Tensile Strength at Yield         13/12.5           MPa                      D 882
  MD/TD
  Ultimate Elongation MD/TD     680/780           %                        D 882
  2% Secant Modulus MD/TD     200/240          MPa                      D 882
  Haze                                     21                   %                        D 1003
  Gloss (45°)                            38                                              D 2457
@ 25 micron film obained on collin 25, B.u.R. 2.5: l, Temp. profile 155 -> 190°C

Note: typical properties, not to be construed as specifications.


 